供应芳纶纤维增强PA66 美国LNP LUBRILOY RA2

芳纶纤维增强尼龙66 LNP LUBRILOY RA2

PA66 美国液氮 RA2

SABIC Innovative Plastics LNP LUBRILOY RA2 PA 66

LNP * LUBRILOY * RA2 是基于含芳纶纤维的尼龙 66 树脂化合物。添加这种材料的特点是： 耐磨损。

物理机械性能：

Physical Properties	Metric	English	Comments
Specific Gravity	1.04 g/cc	1.04 g/cc	ASTM D792
Density	1.05 g/cc	0.0379 lb/in3	ASTM D792
Moisture Absorption	0.200 %	0.200 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	>= 0.020 cm/cm @Time 86400 sec	>= 0.020 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.010 - 0.030 cm/cm @Time 86400 sec	0.010 - 0.030 in/in @Time 24.0 hour	ASTM D955
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	68.0 MPa	9860 psi	Type I, 5 mm/min; ASTM D638
Elongation at Break	4.0 %	4.0 %	Type I, 5 mm/min; ASTM D638
Tensile Modulus	6.89 GPa	999 ksi	5 mm/min; ASTM D638
Flexural Strength	87.0 MPa	12600 psi	ASTM D790
Flexural Modulus	2.62 GPa	380 ksi	1.3 mm/min, 50 mm span; ASTM D790
Compressive Strength	68.0 MPa	9860 psi	SABIC Method
Izod Impact, Notched	0.690 J/cm	1.29 ft-lb/in	ASTM D256
Izod Impact, Unnotched	5.87 J/cm	11.0 ft-lb/in	ASTM D4812
Coefficient of Friction, Dynamic	0.66	0.66	ASTM D3702 Modified
Coefficient of Friction, Static	0.41	0.41	ASTM D3702 Modified
K (wear) Factor	10.1 x 10-8 mm3/N-M	5.00 x 10-10 in3-min/ft-lb-hr	Washer; ASTM D3702 Modified