供应增强无卤阻燃PA6 德国朗盛 BKV20

无卤阻燃PA6 Durethan BKV 20

PA6 德国朗盛 BKV20
Lanxess Durethan BKV 20 FN20 000000 Nylon 6，
 Glass Fiber Reinforced, Flame Retardant
性能特点：PA 6,20%玻璃纤维,注射成型,添加无卤阻燃剂阻燃。

物理/机械性能：

Physical Properties	Metric	English	Comments
Specific Gravity	1.315 g/cc	1.315 g/cc	ISO 1183
Linear Mold Shrinkage, Flow	0.0010 cm/cm	0.0010 in/in	Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
	0.0060 cm/cm	0.0060 in/in	60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse	0.0010 cm/cm	0.0010 in/in	Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
	0.0070 cm/cm	0.0070 in/in	60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	100 MPa	14500 psi	d.a.m.; ISO 527-1, -2; 5 mm/min
Elongation at Break	3.0 %	3.0 %	d.a.m.; ISO 527-1, -2; 5 mm/min
Tensile Modulus	6.10 GPa	885 ksi	d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength	150 MPa @Strain 5.00 %	21800 psi @Strain 5.00 %	d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength	135 MPa @Strain 3.50 %	19600 psi @Strain 3.50 %	d.a.m., 2 mm/min; ISO 178-A
Flexural Modulus	5.70 GPa	827 ksi	d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO)	<= 10.0 kJ/m2	<= 4.76 ft-lb/in2	d.a.m.; ISO 180-1A
Izod Impact, Unnotched (ISO)	30.0 kJ/m2	14.3 ft-lb/in2	d.a.m.; ISO 180-1U