供应通过F1耐候PA6 美国液氮 PX08322
导热耐候级PA6 美国液氮 PX08322
PA6 美国液氮 PX08322
物理性能：
热性能：
SABIC Innovative Plastics LNP KONDUIT PX08322 PA 6
LNP Konduit PX08322 矿物填充尼龙6化合物，导热性和阻燃性能。阻燃UL94-V0，通过F1。
Density
1.52 g/cc
0.0549 lb/in3
ASTM D792
Water Absorption
0.39 %
@Time 86400 sec
0.39 %
@Time 24.0 hour
SABIC Method
Moisture Absorption
0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow
0.0050 cm/cm
@Time 86400 sec
0.0050 in/in
@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse
0.0045 cm/cm
@Time 86400 sec
0.0045 in/in
@Time 24.0 hour
ASTM D955
Melt Flow
15.3 g/10 min
@Load 6.70 kg,
Temperature 285 °C
15.3 g/10 min
@Load 14.8 lb,
Temperature 545 °F
ASTM D1238
CTE, linear, Parallel to Flow
21.5 μm/m-°C
@Temperature -40.0 - 40.0 °C
11.9 μin/in-°F
@Temperature -40.0 - 104 °F
ASTM E 831
27.1 μm/m-°C
@Temperature 40.0 - 120 °C
15.1 μin/in-°F
@Temperature 104 - 248 °F
ASTM E 831
CTE, linear, Transverse to Flow
35.4 μm/m-°C
@Temperature -40.0 - 40.0 °C
19.7 μin/in-°F
@Temperature -40.0 - 104 °F
ASTM E 831
58.3 μm/m-°C
@Temperature 40.0 - 120 °C
32.4 μin/in-°F
@Temperature 104 - 248 °F
ASTM E 831
Thermal Conductivity
0.920 W/m-K
6.38 BTU-in/hr-ft2-°F
through-plane, ?80*3mm discs; ISO 22007-2
2.10 W/m-K
14.6 BTU-in/hr-ft2-°F
through-plane, 10*10*3mm sample; ASTM E 1461-07
5.09 W/m-K
35.3 BTU-in/hr-ft2-°F
in-plane, ?80*3mm discs; ISO 22007-2
8.10 W/m-K
56.2 BTU-in/hr-ft2-°F
in-plane, ?25*0.4mm disc; ASTM E 1461-07
Deflection Temperature at 1.8 MPa (264 psi)
180 °C
@Thickness 6.40 mm
356 °F
@Thickness 0.252 in
unannealed; ASTM D648
Flammability, UL94
V-0
@Thickness 1.20 mm
V-0
@Thickness 0.0472 in
UL 94
Glow Wire Test
825 °C
1520 °F
IEC 60695-2-13
960 °C
@Thickness 1.00 mm
1760 °F
@Thickness 0.0394 in
IEC 60695-2-1